This topic has 11 replies, 8 voices, and was last updated 18 January 2019 at 23:56 by John Reese.

Viewing 12 posts - 1 through 12 (of 12 total)

Author

Posts
18 January 2019 at 10:03 #391679
Brian Abbott
Participant
@brianabbott67793
Hi all.

A little off topic but does anyone know a material which in its raw supplied state is around the 52 – 54 Rc mark ?

Thanks in advance.

Brian
Advert

18 January 2019 at 10:03 #29883
Brian Abbott
Participant
@brianabbott67793
18 January 2019 at 10:22 #391683
Michael Gilligan
Participant
@michaelgilligan61133
According to this page, Brian: **LINK**

Understanding Steel: The Rockwell Hardness Scale

'420' Steel is in your Goldilocks Zone

MichaelG.
18 January 2019 at 13:08 #391709
Anonymous
Plenty of carbon, alloy and stainless steels can meet the requirement after hardening and tempering, but I'm not aware of any sold in a prehardened state. Those that are, like EN16T and EN24T aren't hard enough. There may be some ceramics that meet the requirements, but I haven't looked.

Andrew
18 January 2019 at 13:24 #391710
JasonB
Moderator
@jasonb
What form do you need the material in? Piano wire is only just below that and easily available in small diameters.
18 January 2019 at 15:17 #391725
HOWARDT
Participant
@howardt
Any flame hardening steel will achieve this to some depth, or do you require a through hardened steel. In which case look at the tool steels used for mould making. If its commercial Carrs Steel over Birmingham way are very good at giving you a good selection so long as you can furnish them with correct answers to the questions.
18 January 2019 at 20:06 #391765
Brian Abbott
Participant
@brianabbott67793
Thanks guys for taking the time to repy.

It was something for work, i needed some 25mm thick plate, customer calls for it to be hardened to 52-54, just had something in the back of my mind that there was something available, otherwise i need to heat treat which risks bending the plates.

Not to worry, thanks anyway..
18 January 2019 at 20:15 #391775
Michael Gilligan
Participant
@michaelgilligan61133
Posted by Brian Abbott on 18/01/2019 20:06:29:

Thanks guys for taking the time to repy.

It was something for work, i needed some 25mm thick plate, customer calls for it to be hardened to 52-54, just had something in the back of my mind that there was something available, otherwise i need to heat treat which risks bending the plates.

Not to worry, thanks anyway..

.

… Just curious, Brian … Was my reference to 420 irrelevant to your requirement ?

MichaelG.

.

A little more detail here:

https://springsteelstock.co.uk/stainless-spring-steel/420-stainless-steel/

Edited By Michael Gilligan on 18/01/2019 20:22:05
18 January 2019 at 20:20 #391778
David George 1
Participant
@davidgeorge1
Hi Brian what is it for and what sizes do you need. I have a few different steels

CMS 420 x 35mm dia. P20 x25mm dia. And D2 x 20mm dia.

If any are suitable let me know.

David
18 January 2019 at 20:33 #391789
Anonymous
Posted by Brian Abbott on 18/01/2019 20:06:29:

It was something for work, i needed some 25mm thick plate……….

Seems pretty clear to me?

Andrew
18 January 2019 at 21:21 #391803
colin brannigan
Participant
@colinbrannigan54160
I have used TOOLOX 33 and 44, if I remember rightly that came in at around 420, was used for swaging dies in presses.

Colin
18 January 2019 at 23:56 #391816
John Reese
Participant
@johnreese12848
In the US we have AR500. It is an abrasion resisting plate with a Brinell hardness around 500. Nasty stuff to machine.