Hi Yak, to elaborate, you will be in a world of trouble if you try to harden Silver Steel for this application, ie the shaft will bend and you will get scaling on the outside. In industry a shaft like this would be turned oversize, hardened and then ground to size if you really wanted to heat treat it, but as Iv'e said soft state Silver Steel will be fine.
Tony